This specification covers cold-rolled molybdenum sheet in spinning and deep-drawing quality, produced by rolling pressed and sintered plates.

Up to 800 mm wide, deep-drawing molybdenum sheet is normally supplied in the stress-relieved annealed condition.

After one hour of annealing treatment at 900 ℃ (1073K) in a protective atmosphere, the deep-drawing molybdenum sheet should contain no more than 10% recrystallized material.

The hardness of the deep-drawing molybdenum sheet depends on the degree of deformation.

Deep-drawing molybdenum sheet is free of impurities, splitting, fractures and inclusions.

As for HT-molybdenum sheet, it is produced in thickness of 0.025 mm to 1.0mm. After being completely recrystallized, HT-molybdenum sheet of a thickness of 0.6 to 1.0 mm remains ductile but only in the direction of lamination or lengthwise, for its HT properties are only present in this direction due to the smaller degree of deformation. HT-molybdenum sheet of a thickness of more than 0.6mm should, therefore, only be bent transverse to its direction of lamination or length. HT-molybdenum sheet of a thickness of less than 0.6mm cen be bent, after being recrystallized, in both the longitudinal and transverse directions.