Production Process of Molybdenum Rod

Production process of molybdenum rod: Molding, sintering, draping, machining.

Classification by material:
Pure molybdenum rod: Molybdenum content is greater than 99.95%. High temperature molybdenum rod (Mo La alloy rod): Containing lanthanum 0.4~1.2%, molybdenum content is the margin in addition to impurities. TZM molybdenum rod: Mo-0.5 Ti-0.07~0.12 Zr-0.01~0.04C.

Specifications: Dia(2mm~100mm)*L
1. The surface of sintered molybdenum rod is silver grey metallic luster.
2. The surface of the forged molybdenum rod is coated with a layer of oxide with a black surface.
3. Polished molybdenum rod, silver gray metallic luster.

Surface oxide removal method:
1. Molybdenum products have the characteristics of easy oxidation. When you need to remove the oxide, please entrust the company with strong acid (acid, nitric acid, hydrochloric acid, etc.), please pay attention to the operation.
2. The mild oxide is used as a cleaning agent, which is added with a grinding agent, and is wiped with a soft cloth or sponge, and then washed with warm water. Washed molybdenum products will lose metal luster, please note.

Packaging of molybdenum rods:
Molybdenum rods need to be packaged with PE pearl cotton packaging materials, placed in a suitable wooden box that must be filled with excess space, in order to prevent the occurrence of vibration in transit, damage to the product.



------分隔线----------------------------

Equipments

Electron-beam furnace Vacuum melting furnace Rolling machine
Machining Equipment-3 Sintering Furnace-2 Powder Metallurgy Hydrogen Furnace
Powder Mixer Pressure Embryo Workshop Sintering Furnace-1